Material Properties

Polyvinyl Chloride (PVC) 30% Glass fiber einforced

Material Properties for Polyvinyl Chloride (PVC) 30% Glass fiber einforced

Physical specifications of materials.

Materials Polyvinyl Chloride (PVC) 30% Glass fiber einforced
  Description
Density g/cc 1.58
  lb/in^3 0.05705
Hardness Brinell unless specified 108(Rockwell-R)
Tensile Strength ultimate Mpa 90
  Ksi 13.05
Yield Strength MPa
  Ksi
Modulus of Elasticity Gpa 5
  10^6 Psi 0.72463768
Poisson’s Ratio   0.41
%Elongation at break 2.5
%Reduction of area
Izod Impact J 0.8
  Ft-lb 0.59024
Fracture Toughness Mpa(m)^0.5
  Ksi(in)^0.5
Thermal conductivity W/m-K
  Btu/ft-h-F
Specific Heat Cpacity J/g-K
  Btu/lb-F
Coefficient of thermal expansion 1E-6/K 21
  1E-6/F 11.684210517
Electrical Resistivity Ohm-cm