Material Properties

Carbon Fiber Precursor

Material Properties for Carbon Fiber Precursor

Physical specifications of materials.

Materials Carbon Fiber Precursor
  Description
Density g/cc 1.81
  lb/in^3 0.0654
Hardness Brinell unless specified
Tensile Strength ultimate Mpa 5650
  Ksi 819.25
Yield Strength MPa
  Ksi
Modulus of Elasticity Gpa 290
  10^6 Psi 42.02898544
Poisson’s Ratio  
%Elongation at break 1.8
%Reduction of area
Izod Impact J
  Ft-lb
Fracture Toughness Mpa(m)^0.5
  Ksi(in)^0.5
Thermal conductivity W/m-K 15
  Btu/ft-h-F 8.67052023
Specific Heat Cpacity J/g-K
  Btu/lb-F
Coefficient of thermal expansion 1E-6/K -0.75
  1E-6/F -0.41729323275
Electrical Resistivity Ohm-cm 0.00145